Polymer film comprising a copolyamide of a diamine, a dimer acid and a lactam

ABSTRACT

The present invention relates to a polymer film (P), comprising at least one copolyamide, wherein the copolyamide has been prepared by polymerizing at least one lactam (A) and a monomer mixture (M). The present invention further relates to a process for producing the polymer film (P) and to the use of the polymer film (P) as packaging film.

The present invention relates to a polymer film (P), comprising at least one copolyamide, wherein the copolyamide has been prepared by polymerizing at least one lactam (A) and a monomer mixture (M). The present invention further relates to a process for producing the polymer film (P) and to the use of the polymer film (P) as packaging film.

Polyamides are of particular industrial significance, since they feature very good mechanical properties; more particularly, they have high strength and toughness, good chemical stability and high abrasion resistance. They are used, for example, for production of fishing lines, climbing ropes and carpet backings. In addition, polyamides are employed for production of packaging films and packaging sleeves.

An overview of the use as packaging films and packaging sleeves and on the production thereof is described, for example, in Encyclopedia of Polymer Science and Engineering 2nd ed., vol. 7, pp. 73-127, Vol. 10, pp. 684-695 (John Wiley & Sons, Inc., 1987). However, the polyamide films described therein are very stiff, and have low tear propagation resistance and high density.

For packaging films and packaging sleeves, therefore, copolyamides which combine positive properties of different polyamides are often used. The prior art discloses various copolyamides.

EP 0 352 562 describes films composed of copolyamides, wherein the copolyamides have been prepared from ε-caprolactam and preferably 1 to 10 parts by weight of a dimer acid and a diamine. The copolyamides can then be used for production of flat or blown films. They are likewise suitable for production of composite films.

A disadvantage of the films of copolyamide described in EP 0 352 562 is that they have a relatively low tear propagation resistance, a high modulus of elasticity and a low puncture energy.

DE 28 46 596 describes shaped bodies made from a copolyamide formed from caprolactam, fatty acid dimers and hexamethylenediamine. However, the thermoplastics described cannot be extruded to a film.

It was an object of the present invention to provide a polymer film that comprises a polyamide and has the disadvantages of the polymer films described in the prior art only to a reduced degree, if at all. The polymer film should additionally be producible in a very simple and inexpensive manner.

This object is achieved by a polymer film (P) comprising at least one copolyamide prepared by polymerizing the following components:

-   (A) 15% to 84% by weight of at least one lactam, -   (B) 16% to 85% by weight of a monomer mixture (M) comprising the     following components:     -   (B1) at least one C₃₂-C₄₀ dimer acid and     -   (B2) at least one C₄-C₁₂ diamine,         where the percentages by weight of components (A) and (B) are         each based on the sum total of the percentages by weight of         components (A) and (B).

It has been found that, surprisingly, the polymer film (P) of the invention has high tear propagation resistance both in extrusion direction and at right angles thereto. This is particularly advantageous when the polymer film (P) of the invention is used as packaging film.

Furthermore, the polymer film (P) of the invention has high transparency, and high low-temperature toughness. It is additionally advantageous that the polymer film (P) of the invention is less stiff than the polymer films (P) described in the prior art that comprise a polyimide or a copolyamide. The polymer film (P) of the invention also has a low modulus of elasticity and a high puncture resistance in the dry state. The high puncture resistance is likewise of particular significance when the polymer film (P) is used as packaging film.

The invention is elucidated in detail hereinafter.

Polymer Film (P)

According to the invention, the polymer film (P) comprises at least one copolyamide.

In the context of the present invention, “at least one copolyamide” is understood to mean either exactly one copolyamide or a mixture of two or more copolyamides.

The polymer film (P) has a thickness, for example, in the range from 0.1 μm to 1 mm, preferably a thickness in the range from 5 to 500 μm and especially preferably in the range from 20 to 100 μm.

The present invention therefore also provides a polymer film (P) in which the polymer film (P) has a thickness in the range from 0.1 μm to 1 mm.

The polymer film (P) may, in addition to the at least one copolyamide, comprise at least one further polymer (FP).

In the context of the present invention, “at least one further polymer (FP)” means either exactly one further polymer (FP) or a mixture of two or more further polymers (FP).

Polymers suitable as the at least one further polymer (FP) are all polymers known to those skilled in the art. It will be apparent that the at least one further polymer (FP) is different than the at least one copolyamide.

Preferably, the at least one further polymer (FP) is selected from the group consisting of polyolefins, poly(ethyl-vinyl alcohols), poly(ethyl-vinyl acetates), polyethylene terephthalates, polyvinylidene chlorides, maleic anhydride-grafted polyolefins, polyesters and ionomers. More preferably, the at least one further polymer (FP) is selected from the group consisting of polyolefins, poly(ethyl-vinyl alcohols), poly(ethyl-vinyl acetates), polyethylene terephthalates, polyvinylidene chlorides and maleic anhydride-grafted polyolefins. Most preferably, the at least one further polymer (FP) is selected from the group consisting of polyolefins, maleic anhydride-grafted polyolefins and ethyl-vinyl alcohols.

If the at least one further polymer (FP) is selected from the group consisting of polyolefins, it is preferable that, in addition, maleic anhydride-grafted polyolefins are used as at least one further polymer (FP). It is possible here that the at least one further polymer (FP) used is a mixture of polyolefins and maleic anhydride-grafted polyolefins. It is likewise possible that, when the polymer film (P) is a multilayer film described below, the polymer film (P) comprises at least one first further layer of at least one further polymer (FP), where the at least one further polymer (FP) of the first further layer is selected from the group consisting of maleic anhydride-grafted polyolefins and the polymer film (P) comprises at least one second further layer of at least one further polymer (FP), where the at least one further polymer (FP) of the second further layer is selected from the group consisting of polyolefins. The polymer film (P) in that case preferably comprises the first further layer between the first layer comprising the at least one copolyamide and the second further layer.

Polyolefins as such are known to those skilled in the art. Preferred polyolefins are polypropylene (PP), low-density polyethylene (LDPE), linear low-density polyethylene (LLDPE) and very low-density polyethylene (VLDPE).

Linear low-density polyethylene (LLDPE) is a copolymer of ethylene and at least one C₄-C₈-α-olefin. Linear low-density polyethylene (LLDPE) features long polymer chains with short side chains. The length of the side chains in linear low-density polyethylene (LLDPE) is typically shorter than in low-density polyethylene (LDPE) and in medium-density polyethylene (MDPE). The melting point of linear low-density polyethylene (LLDPE) is preferably in the range from 110 to 130° C.; its density is in the range from 0.91 to 0.93 g/cm³.

Very low-density polyethylenes (VLDPE) are copolymers of ethylene and at least one C₄-C₈-α-olefin. They typically have a melting point in the range from 110 to 130° C. and a density in the range from 0.86 to <0.91 g/cm³. The proportion of C₄-C₈-α-olefins in VLDPE is generally higher than in LLDPE.

In the contact of the present invention, “C₄-C₈-α-olefin” is understood to mean linear and branched, preferably linear, alkylenes having 4 to 8 carbon atoms that are unsaturated in the α position, i.e. have a C—C double bond in the α position. Examples of these are 1-butene, 1-pentene, 1-hexene, 1-heptene and 1-octene. 1-Butene, 1-hexene and 1-octene are preferred.

Preferred poly(ethylene-vinyl acetates) are copolymers of ethylene with vinyl acetate. For example, they are prepared using in the range from 82% to 99.9% by weight of ethylene and in the range from 0.1% to 18% by weight of vinyl acetate, preferably in the range from 88% to 99.9% by weight of ethylene and in the range from 0.1% to 12% by weight of vinyl acetate.

Preferred poly(ethylene-vinyl alcohols) are obtainable by complete or partial hydrolysis of the above-described poly(ethylene-vinyl acetates). For example, the poly(ethylene-vinyl alcohols) comprise in the range from 50 to 75 mol % of ethylene and in the range from 25 to 50 mol % of vinyl alcohol, based on the total molar amount of the poly(ethylene-vinyl alcohols).

The polymer film (P) may comprise the at least one further polymer (FP) as a blend (mixture) with the at least one copolyamide.

Furthermore, it is possible and preferable in accordance with the invention that the polymer film (P) comprises at least one first layer comprising the at least one copolyamide, and the polymer film (P) comprises at least one further layer comprising the at least one further polymer (FP).

In this embodiment, it is preferable that the at least one first layer comprising the at least one copolyamide does not comprise any further polymer (FP).

In the context of the present invention, “at least one first layer” means either exactly one first layer or two or more first layers.

In the context of the present invention, “at least one further layer” means either exactly one further layer or two or more further layers. Two or more further layers are preferred.

It is thus preferable that the polymer film (P) comprises at least one first layer comprising the at least one copolyamide, and the polymer film (P) also comprises at least one further layer, where the at least one further layer comprises at least one further polymer (FP) selected from the group consisting of polyolefins, poly(ethylene-vinyl alcohols), poly(ethylene-vinyl acetates), polyethylene terephthalates, polyvinylidene chlorides and maleic anhydride-grafted polyolefins.

The present invention thus also provides a polymer film (P), in which the polymer film (P) comprises at least one first layer comprising the at least one copolyamide, and the polymer film (P) comprises at least one further layer, where the at least one further layer comprises at least one further polymer (FP) selected from the group consisting of polyolefins, poly(ethylene-vinyl alcohols), polyethylene-vinyl acetates), polyethylene terephthalates, polyvinylidene chlorides and maleic anhydride-grafted polyolefins.

If the polymer film (P), apart from the at least one first layer, does not comprise any further layer, the polymer film (P) is also referred to as a monofilm. If the polymer film (P) is a monofilm, it may comprise exactly one first layer and no further layer; it is likewise possible that it comprises two or more first layers and no further layer. If the polymer film (P) comprises two or more first layers and is a monofilm, the two or more first layers all have the same composition.

If the polymer film (P) comprises at least one first layer comprising the at least one copolyamide, and at least one further layer comprising the at least one further polymer (FP), the polymer film (P) is also referred to as a multilayer film.

For example, the polymer film (P) in that case comprises 1 to 11 first layers comprising the at least one copolyamide, and 1 to 13 further layers comprising the at least one further polymer (FP). Preferably, the polymer film (P) comprises 1 to 5 first layers comprising the at least one copolyamide, and 1 to 11 further layers comprising the at least one further polymer (FP). Especially preferably, the polymer film (P) comprises 1 to 3 first layers comprising the at least one copolyamide, and 1 to 7 further layers comprising the at least one further polymer (FP).

In a preferred embodiment of the present invention, the at least one first layer consists of the at least one copolyamide. It is likewise preferable that the at least one further layer consists of the at least one further polymer (FP).

In the context of the present invention, the term “polymer film (P)” thus comprises both monofilms and multilayer films.

The present invention therefore also provides a polymer film (P), wherein the polymer film (P) is a monofilm or a multilayer film.

As described above, the polymer film (P) typically has a thickness in the range from 0.1 μm to 1 mm, preferably in the range from 5 to 500 μm and especially preferably in the range from 10 to 100 μm.

If the polymer film (P) is a monofilm and comprises exactly one first layer, the first layer has the same thickness as the polymer film (P), i.e., for example, in the range from 0.1 μm to 1 mm, preferably in the range from 5 to 500 μm and especially preferably in the range from 10 to 100 μm. If the polymer film (P) is a monofilm and comprises two or more first layers, the thickness of every first layer is typically less than the thickness of the polymer film (P). The sum total of the thicknesses of the individual first layers in that case generally corresponds to the thickness of the polymer film (P). For example, the at least one first layer comprising the at least one copolyamide in that case has a thickness in the range from 0.1 to 100 μm, preferably in the range from 0.5 to 50 μm and especially preferably in the range from 0.5 to 15 μm.

If the polymer film (P) is a multilayer film, the thickness of the individual layers of the polymer film (P), i.e. the thickness of the at least one first layer comprising the at least one copolyamide, and the thickness of the at least one further layer comprising the at least one further polymer (FP), is typically less than the thickness of the polymer film (P). The sum total of the thicknesses of the individual layers in that case generally corresponds to the thickness of the polymer film (P).

For example, the at least one first layer comprising the at least one copolyamide in that case has a thickness in the range from 0.1 to 100 μm, preferably in the range from 0.5 to 50 μm and especially preferably in the range from 0.5 to 15 μm.

The at least one further layer comprising the at least one further polymer (FP) in that case has a thickness, for example, in the range from 0.1 to 100 μm, preferably in the range from 0.5 to 50 μm and especially preferably in the range from 0.5 to 15 μm.

The polymer film (P) may comprise at least one adhesion promoter. This embodiment is preferred when the polymer film (P) is a multilayer film.

In the context of the present invention, “at least one adhesion promoter” means either exactly one adhesion promoter or a mixture of two or more adhesion promoters.

If the polymer film (P) is a multilayer film, the at least one adhesion promoter may be present together with the at least one copolyamide in the at least one first layer. It is likewise possible that the at least one adhesion promoter is present together with the at least one further polymer (FP) in the at least one further layer. Furthermore, it is possible that the at least one adhesion promoter is present as at least one additional layer in the polymer film (P). This embodiment is preferred.

When the at least one adhesion promoter is present as at least one additional layer in the polymer film (P), this at least one additional layer is preferably arranged between the at least one further layer comprising the at least one further polymer (FP), and the at least one first layer comprising the at least one copolyamide. The at least one layer of the adhesion promoter has a thickness, for example, of 0.1 to 100 μm, preferably in the range from 0.5 to 50 μm and especially preferably in the range from 0.5 to 15 μm.

Suitable adhesion promoters are known as such to the person skilled in the art. Preferred adhesion promoters are copolymers of ethylene with maleic anhydride or a copolymer of ethylene with vinyl acetate. Preference is given to a copolymer of linear low-density polyethylene (LLDPE) and maleic anhydride or a copolymer of ethylene and vinyl acetate, the copolymer being prepared using >18% by weight of vinyl acetate and <82% by weight of ethylene. These copolymers are commercially available, for example under the Bynel 4105 trade name from DuPont or Escorene FL00119 from Exxon.

Copolymers of ethylene with maleic anhydride that are used with preference as adhesion promoters are maleic anhydride-grafted polymers or copolymers of ethylene.

The polymer film (P) may also comprise additives. Additives of this kind are known to those skilled in the art and are selected, for example, from the group consisting of stabilizers, dyes, antistats, tackifiers, anti-blockers, processing auxiliaries, antioxidants, light stabilizers, UV absorbers, lubricants and nucleating aids.

Suitable dyes are organic and inorganic pigments, for example titanium dioxide provided with a size. Suitable tackifiers are, for example, polyisobutylene (PIB) or ethyl-vinyl acetate (EVA). Suitable antiblocking agents are, for example, silicon dioxide particles or calcium carbonate particles. Suitable light stabilizers are, for example, what are called HALS (hindered amine light stabilizers). Processing auxiliaries or lubricants used may, for example, be ethylenebisstearamide (EBS) wax. Nucleating aids may, for example, be all kinds of organic or inorganic crystallization nucleators, for example talc.

The additives may either be present either in the at least one first layer or in the at least one further layer. They may be present in just one of these layers; it is likewise possible that they are present in each of these layers.

Copolyamide

According to the invention, the polymer film (P) comprises at least one copolyamide prepared by polymerizing the following components:

-   (A) 15% to 84% by weight of at least one lactam, -   (B) 16% to 85% by weight of a monomer mixture (M) comprising the     following components:     -   (B1) at least one C₃₂-C₄₀ dimer acid and     -   (B2) at least one C₄-C₁₂ diamine,         where the percentages by weight of components (A) and (B) are         each based on the sum total of the percentages by weight of         components (A) and (B).

The terms “component (A)” and “at least one lactam” are used synonymously in the context of the present invention and therefore have the same meaning.

The same applies to the terms “component (B)” and “a monomer mixture (M)”. These terms are likewise used synonymously in the context of the present invention and therefore have the same meaning.

In the context of the present invention, “at least one lactam” means either exactly one lactam or a mixture of two or more lactams. Preference is given to exactly one lactam.

According to the invention, the at least one copolyamide has been prepared by polymerizing 15% to 84% by weight of component (A) and 16% to 85% by weight of component (B); preferably, the copolyamide has been prepared by polymerizing 40% to 83% by weight of component (A) and from 17% to 60% by weight of component (B); especially preferably, the at least one copolyamide has been prepared by polymerizing from 60% to 80% by weight of component (A) and 20% to 40% by weight of component (B), where the percentages by weight of components (A) and (B) are each based on the sum total of the percentages by weight of components (A) and (B).

Preferably, the sum total of the percentages by weight of components (A) and (B) adds up to 100% by weight.

It will be apparent that the percentages by weight of components (A) and (B) are based on the percentages by weight of components (A) and (B) prior to polymerization, i.e. when components (A) and (B) have not yet reacted with one another. During the polymerization, the weight ratio of components (A) and (B) may change.

According to the invention, the copolyamide is prepared by polymerizing components (A) and (B). The polymerization of components (A) and (B) is known to those skilled in the art. Typically, the polymerization of components (A) with (B) is a condensation reaction. During the condensation reaction, component (A) reacts with components (B1) and (B2) present in component (B) and with any component (B3) as described further down that may likewise be present in component (B). This forms amide bonds between the individual components. Typically, component (A) is at least partly in open-chain form during the polymerization, i.e. in the form of an amino acid.

The polymerization of components (A) and (B) may take place in the presence of a catalyst. Suitable catalysts are all catalysts that are known to those skilled in the art and catalyze the polymerization of components (A) and (B). Catalysts of this kind are known to those skilled in the art. Preferred catalysts are phosphorus compounds, for example sodium hypophosphite, phosphorous acid, triphenylphosphine or triphenyl phosphite.

The polymerization of components (A) and (B) forms the copolyamide, which therefore receives structural units derived from component (A) and structural units derived from component (B). Structural units derived from component (B) comprise structural units derived from components (B1) and (B2) and from any component (B3).

The polymerization of components (A) and (B) forms the copolyamide as the copolymer. The copolymer may be a random copolymer; it is likewise possible that it is a block copolymer.

In a block copolymer, there is formation of blocks of units derived from component (B) and of blocks of units derived from component (A). These alternate. In the case of a random copolymer, there is alternation of structural units derived from component (A) with structural units derived from component (B). This alternation is random; for example, two structural units derived from component (B) may be followed by one structural unit derived from component (A), which is in turn followed by one structural unit derived from component (B), which is then followed by a structural unit comprising three structural units derived from component (A).

Preferably, the at least one copolyamide is a random copolymer.

The present invention therefore also provides a polymer film (P) in which the at least one copolyamide is a random copolymer.

The preparation of the at least one copolyamide preferably comprises the following steps:

-   a) polymerizing components (A) and (B) to obtain at least one first     copolyamide, -   b) pelletizing the at least one first copolyamide obtained in     step a) to obtain at least one pelletized copolyamide, -   c) extracting the at least one pelletized copolyamide obtained in     step b) with water to obtain at least one extracted copolyamide, -   d) drying the at least one extracted copolyamide obtained in step c)     at a temperature (T_(T)) to obtain the at least one copolyamide.

The present invention therefore also provides a polymer film (P) in which the copolyamide is prepared in a process comprising the following steps:

-   a) polymerizing components (A) and (B) to obtain at least one first     copolyamide, -   b) pelletizing the at least one first copolyamide obtained in     step a) to obtain at least one pelletized copolyamide, -   c) extracting the at least one pelletized copolyamide obtained in     step b) with water to obtain at least one extracted copolyamide, -   d) drying the at least one extracted copolyamide obtained in step c)     at a temperature (T_(T)) to obtain the at least one copolyamide.

The polymerization in step a) can take place in any reactors known to those skilled in the art. Preference is given to stirred tank reactors. It is additionally possible to use auxiliaries known to those skilled in the art to improve the reaction regime, for example defoamers such as polydimethylsiloxane (PDMS).

In step b), the at least one first copolyamide obtained in step a) can be pelletized by any methods known to those skilled in the art, for example by means of strand pelletization or underwater pelletization.

The extraction in step c) can be effected by any methods known to those skilled in the art.

During the extraction in step c), by-products that are typically formed during the polymerization of components (A) and (B) in step a) are extracted from the at least one pelletized copolyamide.

In step d), the at least one extracted copolyamide obtained in step c) is dried. Methods of drying are known to those skilled in the art. According to the invention, the at least one extracted copolyamide is dried at a temperature (T_(T)). The temperature (T_(T)) is preferably above the glass transition temperature (T_(G(C))) of the at least one copolyamide and below the melting temperature (T_(M(C))) of the at least one copolyamide.

The drying in step d) is typically effected for a period of time in the range from 1 to 100 hours, preferably in the range from 2 to 50 hours and especially preferably in the range from 3 to 40 hours.

It is envisaged that the drying in step d) will further increase the molecular weight of the at least one copolyamide.

The at least one copolyamide typically has a glass transition temperature (T_(G(C))). The glass transition temperature (T_(G(C))) is, for example, in the range from 20 to 50° C., preferably in the range from 23 to 47° C. and especially preferably in the range from 25 to 45° C., determined according to ISO 11357-2: 2014.

The present invention therefore also provides a polymer film (P) in which the at least one copolyamide has a glass transition temperature (T_(G(C))), where the glass transition temperature (T_(G(C))) is in the range from 20 to 50° C.

The glass transition temperature (T_(G(C))) of the at least one copolyamide, in accordance with ISO 11357-2: 2014, in the context of the present invention, is based on the glass transition temperature (T_(G(C))) of the dry copolyamide.

In the context of the present invention, “dry” means that the at least one copolyamide comprises less than 1% by weight, preferably less than 0.5% by weight and especially preferably less than 0.1% by weight of water, based on the total weight of the at least one copolyamide. More preferably, “dry” means that the at least one copolyamide does not comprise any water and most preferably that the at least one copolyamide does not comprise any solvent.

The at least one copolyamide additionally has a melting temperature (T_(M(C))). The melting temperature (T_(M(C))) of the at least one copolyamide is, for example, in the range from 150 to 210° C., preferably in the range from 160 to 205° C. and especially preferably in the range from 160 to 200° C., determined according to ISO 11357-3: 2014.

The present invention therefore also provides a polymer film (P) in which the at least one copolyamide has a melting temperature (T_(M(C))), where the melting temperature (T_(M(C))) is in the range from 150 to 210° C.

The at least one copolyamide generally has a viscosity number (VN_((C))) in the range from 150 to 300 mL/g, determined in a 0.5% by weight solution of the at least one copolyamide in a mixture of phenol/o-dichlorobenzene in a weight ratio of 1:1.

Preferably, the viscosity number (VN_((C))) of the at least one copolyamide is in the range from 160 to 290 mL/g and more preferably in the range from 170 to 280 mL/g, determined in a 0.5% by weight solution of the at least one copolyamide in a mixture of phenol/o-dichlorobenzene in a weight ratio of 1:1.

The present invention therefore also provides a polymer film (P) in which the at least one copolyamide has a viscosity number (VN_((C))) in the range from 150 to 300 mL/g, determined in a 0.5% by weight solution of the at least one copolyamide in a mixture of phenol/o-dichlorobenzene in a weight ratio of 1:1.

Component (A)

Component (A) is at least one lactam.

Lactams are known as such to those skilled in the art. Preference is given in accordance with the invention to lactams having 4 to 12 carbon atoms.

In the context of the present invention, lactams are understood to mean cyclic amides having, in the ring, preferably 4 to 12 and more preferably 5 to 8 carbon atoms.

Suitable lactams are selected, for example, from the group consisting of 3-aminopropanolactam (propio-3-lactam; β-lactam; β-propiolactam), 4-aminobutanolactam (butyro-4-lactam; γ-lactam; γ-butyrolactam), 5-aminopentanolactam (2-piperidinone; δ-lactam; δ-valerolactam), 6-aminohexanolactam (hexano-6-lactam: ε-lactam; ε-caprolactam), 7-aminoheptanolactam (heptano-7-lactam; ζ-lactam; ζ-heptanolactam), 8-aminooctanolactam (octano-8-lactam; η-lactam; η-octanolactam), 9-aminononanolactam (nonano-9-lactam; θ-lactam; θ-nonanolactam), 10-aminodecanolactam (decano-10-lactam; ω-decanolactam), 11-aminoundecanolactam (undecano-11-lactam; ω-undecanolactam) and 12-aminododecanolactam (dodecano-12-lactam; ω-dodecanolactam).

The present invention therefore also provides a polymer film (P) in which component (A) is selected from the group consisting of 3-aminopropanolactam, 4-aminobutanolactam, 5-aminopentanolactam, 6-aminohexanolactam, 7-aminoheptanolactam, 8-aminooctanolactam, 9-aminononanolactam, 10-aminodecanolactam, 11-aminoundecanolactam and 12-aminododecanolactam.

The lactams may be unsubstituted or at least monosubstituted. If at least monosubstituted lactams are used, these may bear, on the nitrogen atom and/or on the carbon atoms of the ring, one, two or more substituents independently selected from the group consisting of C₁- to C₁₀-alkyl, C₅- to C₆-cycloalkyl and C₅- to C₁₀-aryl.

Suitable C₁- to C₁₀-alkyl substituents are, for example, methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl and tert-butyl. An example of a suitable C₅- to C₆-cycloalkyl substituent is cyclohexyl. Preferred C₅- to C₁₀-aryl substituents are phenyl and anthranyl.

Preference is given to using unsubstituted lactams, preference being given to γ-lactam (γ-butyrolactam), δ-lactam (δ-valerolactam) and ε-lactam (ε-caprolactam). Particular preference is given to δ-lactam (δ-valerolactam) and ε-lactam (ε-caprolactam), especial preference to ε-caprolactam.

Monomer Mixture (M)

According to the invention, component (B) is a monomer mixture (M). The monomer mixture (M) comprises components (B1), at least one C₃₂-C₄₀ dimer acid and (B2) at least one C₄-C₁₂ diamine.

In the context of the present invention, a monomer mixture (M) is understood to mean a mixture of two or more monomers, where at least components (B1) and (B2) are present in the monomer mixture (M).

In the context of the present invention, the terms “component (B1)” and “at least one C₃₂-C₄₀ dimer acid” are used synonymously and therefore have the same meaning. The same applies to the terms “component (B2)” and “at least one C₄-C₁₂ diamine”. These terms are likewise used synonymously in the context of the present invention and therefore have the same meaning.

The monomer mixture (M) comprises, for example, in the range from 45 to 55 mol % of component (B1) and in the range from 45 to 55 mol % of component (B2), based in each case on the sum total of the molar percentages of components (B1) and (B2), preferably based on the total molar amount of component (B).

Preferably, component (B) comprises in the range from 47 to 53 mol % of component (B1) and in the range from 47 to 53 mol % of component (B2), based in each case on the sum total of the molar percentages of components (B1) and (B2), preferably based on the total molar amount of component (B).

More preferably, component (B) comprises in the range from 49 to 51 mol % of component (B1) and in the range from 49 to 51 mol % of component (B2), based in each case on the sum total of the molar percentages of components (B1) and (B2), preferably based on the total molar amount of component (B).

The present invention therefore also provides a polymer film (P) in which component (B) comprises in the range from 45 to 55 mol % of component (B1) and in the range from 45 to 55 mol % of component (B2), based in each case on the total molar amount of component (B).

The sum total of the molar percentages of components (B1) and (B2) present in component (B) typically adds up to 100 mol %.

Component (B) may also additionally comprise a component (B3), at least one C₄-C₂₀ diacid.

The present invention therefore also provides a polymer film (P) in which component (B) additionally comprises a component (B3), at least one C₄-C₂₀ diacid.

The terms “component (B3)” and “at least one C₄-C₂₀ diacid” are used synonymously in the context of the present invention and therefore have the same meaning.

When component (B) additionally comprises component (B3), it is preferable that component (B) comprises in the range from 25 to 54.9 mol % of component (B1), in the range from 45 to 55 mol % of component (B2) and in the range from 0.1 to 25 mol % of component (B3), based in each case on the total molar amount of component (B).

More preferably, component (B) in that case comprises in the range from 13 to 52.9 mol % of component (B1), in the range from 47 to 53 mol % of component (B2) and in the range from 0.1 to 13 mol % of component (B3), based in each case on the total molar amount of component (B).

Most preferably, component (B) in that case comprises in the range from 7 to 50.9 mol % of component (B1), in the range from 49 to 51 mol % of component (B2) and in the range from 0.1 to 7 mol % of component (B3), based in each case on the total molar amount of component (B).

When component (B) additionally comprises component (B3), the molar percentages of components (B1), (B2) and (B3) typically add up to 100 mole percent.

The monomer mixture (M) may additionally comprise water.

Components (B1) and (B2) and optionally (83) of component (B) may react with one another to obtain amides. This reaction is known as such to those skilled in the art. Therefore, component (B) may comprise components (B1) and (B2) and optionally (B3) in fully reacted form, in partly reacted form or in unreacted form. Preferably, component (B) comprises components (B1) and (B2) and optionally (B3) in unreacted form.

In the context of the present invention, “in unreacted form” thus means that component (B1) is present in the form of the at least one C₃₂-C₄₀ dimer acid and component (B2) in the form of the at least one C₄-C₁₂ diamine and, if appropriate, component (B3) in the form of the at least one C₄-C₂₀ diacid.

If components (B1) and (B2) and, if appropriate, (B3) have at least partly reacted with one another, components (B1) and (B2) and, if appropriate, (B3) are at least partly in amide form.

Component (B1)

According to the invention, component (B1) is at least one C₃₂-C₄₀ dimer acid.

In the context of the present invention, “at least one C₃₂-C₄₀ dimer acid” means either exactly one C₃₂-C₄₀ dimer acid or a mixture of two or more C₃₂-C₄₀ dimer acids.

Dimer acids are also referred to as dimer fatty acids. C₃₂-C₄₀ dimer acids are known as such to those skilled in the art and are typically prepared by dimerization of unsaturated fatty acids. This dimerization can be catalyzed, for example, by aluminas.

Suitable unsaturated fatty acids for preparation of the at least one C₃₂-C₄₀ dimer acid are known to those skilled in the art and are, for example, unsaturated C₁₆ fatty acids, unsaturated C₁₈ fatty acids and unsaturated C₂₀ fatty acids.

Preferably, component (B1) is therefore prepared proceeding from unsaturated fatty acids selected from the group consisting of unsaturated C₁₆ fatty acids, unsaturated C₁₈ fatty acids and unsaturated C₂₀ fatty acids, particular preference being given to the unsaturated C₁₈ fatty acids.

The present invention therefore also provides a polymer film (P) in which component (B1) is prepared proceeding from unsaturated fatty acids selected from the group consisting of unsaturated C₁₆ fatty acids, unsaturated C₁₈ fatty acids and unsaturated C₂₀ fatty acids.

An example of a suitable unsaturated C₁₆ fatty acid is palmitoleic acid ((9Z)-hexadeca-9-enoic acid).

Suitable unsaturated C₁₈ fatty acids are selected, for example, from the group consisting of petroselic acid ((6Z)-octadeca-6-enoic acid), oleic acid ((9Z)-octadeca-9-enoic acid), elaidic acid ((9E)-octadeca-9-enoic acid), vaccenic acid ((11E)-octadeca-11-enoic acid), linoleic acid ((9Z,12Z)-octadeca-9,12-dienoic acid), alpha-linolenic acid ((9Z,12Z,15Z)-octadeca-9,12,15-trienoic acid), gamma-linolenic acid ((6Z,9Z,12Z)-octadeca-6,9,12-trienoic acid), calendic acid ((8E,10E,12Z)-octadeca-8,10,12-trienoic acid), punicic acid ((9Z,11E,13Z)-octadeca-9,11,13-trienoic acid), alpha-eleostearic acid ((9Z,11E,13E)-octadeca-9,11,13-trienoic acid) and beta-eleostearic acid ((9E,11E,13E)-octadeca-9,11,13-trienoic acid). Particular preference is given to unsaturated C₁₈ fatty acids selected from the group consisting of petroselic acid ((6Z)-octadeca-6-enoic acid), oleic acid ((9Z)-octadeca-9-enoic acid), elaidic acid ((9E)-octadeca-9-enoic acid), vaccenic acid ((11E)-octadeca-11-enoic acid), linoleic acid ((9Z,12Z)-octadeca-9,12-dienoic acid).

Suitable unsaturated C₂₀ fatty acids are selected, for example, from the group consisting of gadoleic acid ((9Z)-eicosa-9-enoic acid), eicosenoic acid ((11Z)-eicosa-11-enoic acid), arachidonic acid ((5Z,8Z,11Z,14Z)-eicosa-5,8,11,14-tetraenoic acid) and timnodonic acid ((5Z,8Z,11Z,14Z,17Z)-eicosa-5,8,11,14,17-pentaenoic acid).

Component (B1) is especially preferably at least one C₃₆ dimer acid.

The at least one C₃₆ dimer acid is preferably prepared proceeding from unsaturated C₁₈ fatty acids. More preferably, the C₃₆ dimer acid is prepared proceeding from C₁₃ fatty acids selected from the group consisting of petroselic acid ((6Z)-octadeca-6-enoic acid), oleic acid ((9Z)-octadeca-9-enoic acid), elaidic acid ((9E)-octadeca-9-enoic acid), vaccenic acid ((11E)-octadeca-11-enoic acid) and linoleic acid ((9Z,12Z)-octadeca-9,12-diensäure).

In the preparation of component (B1) from unsaturated fatty acids, trimer acids may additionally form; residues of unreacted unsaturated fatty acid may also remain.

The formation of trimer acids is known to those skilled in the art.

Preferably in accordance with the invention, component (B1) comprises not more than 0.5% by weight of unreacted unsaturated fatty acid and not more than 0.5% by weight of trimer acid, more preferably not more than 0.2% by weight of unreacted unsaturated fatty acid and not more than 0.2% by weight of trimer acid, based in each case on the total weight of component (B1).

Dimer acids (also known as dimerized fatty acids or dimer fatty acids) thus refer generally and especially in the context of the present invention to mixtures that are prepared by oligomerization of unsaturated fatty acids. They are preparable, for example, by catalytic dimerization of unsaturated fatty acids from vegetable sources, in which case the starting materials used are especially unsaturated C₁₆ to C₂₀ fatty acids. The addition is primarily of the Diels-Alder type, and the result, according to the number and position of the double bonds in the fatty acids used for preparation of the dimer acids, is mixtures of primarily dimeric products having cycloaliphatic, linear aliphatic, branched aliphatic and also C₆-aromatic hydrocarbyl groups between the carboxyl groups. According to the mechanism and/or any subsequent hydrogenation, the aliphatic radicals may be saturated or unsaturated, and the proportion of aromatic groups may also vary. The radicals between the carboxylic acid groups in that case comprise, for example, 32 to 40 carbon atoms. Preference is given to using fatty acids having 18 carbon atoms for the preparation, such that the dimeric product thus has 36 carbon atoms. Preferably, the radicals that connect the carboxyl groups of the dimer fatty acids do not have any unsaturated bonds or any aromatic hydrocarbyl radicals.

In the context of the present invention, C₁₈ fatty acids are thus preferably used in the preparation. Particular preference is given to using linolenic acid, linoleic acid and/or oleic acid.

Depending on the reaction regime, the oligomerization described above gives rise to mixtures comprising mainly dimeric molecules, but also trimeric molecules and also monomeric molecules and other by-products. Purification is typically by distillative means. Commercial dimer acids generally comprise at least 80% by weight of dimeric molecules, up to 19% by weight of trimeric molecules and not more than 1% by weight of monomeric molecules and other by-products.

It is preferable to use dimer acids consisting of dimeric fatty acid molecules to an extent of at least 90% by weight, preferably to an extent of at least 95% by weight, even more preferably to an extent of at least 98% by weight.

The proportions of monomeric, dimeric and trimeric molecules and other by-products in the dimer acids can be determined, for example, by means of gas chromatography (GC). The dimer acids here, prior to the GC analysis, are converted to the corresponding methyl esters via the boron trifluoride method (cf. DIN EN ISO 5509) and then analyzed by means of GC.

A fundamental characteristic of “dimer acids” in the context of the present invention is thus that the preparation thereof comprises the oligomerization of unsaturated fatty acids. This oligomerization gives rise primarily to dimeric products, i.e. preferably to an extent of at least 80% by weight, more preferably to an extent of at least 90% by weight, even more preferably to an extent of at least 95% by weight and especially to an extent of at least 98% by weight. The fact that the oligomerization thus gives rise predominantly to dimeric products comprising exactly two fatty acid molecules justifies this name, which is in common use in any case. An alternative expression for the term “dimer acids” in question is thus “mixture comprising dimerized fatty acids”.

The dimer acids to be used are obtainable as commercial products. Examples of these include Radiacid 0970, Radiacid 0971, Radiacid 0972, Radiacid 0975, Radiacid 0976 and Radiacid 0977 from Oleon, Pripol 1006, Pripol 1009, Pripol 1012, and Pripol 1013 from Croda, Empol 1008, Empol 1012, Empol 1061 and Empol 1062 from BASF SE, and Unidyme 10 and Unidyme TI from Arizona Chemical.

Component (B1) has an acid number, for example, in the range from 190 to 200 mg KOH/g.

Component (B2)

According to the invention, component (B2) is at least one C₄-C₁₂ diamine.

In the context of the present invention, “at least one C₄-C₁₂ diamine” means either exactly one C₄-C₁₂ diamine or a mixture of two or more C₄-C₁₂ diamines.

In the context of the present compound, “C₄-C₁₂ diamine” is understood to mean aliphatic and/or aromatic compounds having four to twelve carbon atoms and two amino groups (—NH₂ groups). The aliphatic and/or aromatic compounds may be unsubstituted or additionally at least monosubstituted. If the aliphatic and/or aromatic compounds are additionally at least monosubstituted, they may bear one, two or more substituents that do not take part in the polymerization of components (A) and (B). Substituents of this kind are, for example, alkyl or cycloalkyl substituents. These are known as such to those skilled in the art. The at least one C₄-C₁₂ diamine is preferably unsubstituted.

Suitable components (B2) are selected, for example, from the group consisting of 1,4-diaminobutane (butane-1,4-diamine; tetramethylenediamine; putrescine), 1,5-diaminopentane (pentamethylenediamine; pentane-1,5-diamine; cadaverine), 1,6-diaminohexane (hexamethylenediamine; hexane-1,6-diamine), 1,7-diaminoheptane, 1,8-diaminoctane, 1,9-diaminononane, 1,10-diaminodecane (decamethylenediamine), 1,11-diaminoundecane (undecamethylenediamine) and 1,12-diaminododecane (dodecamethylenediamine).

Preferably, component (B2) is selected from the group consisting of tetramethylenediamine, pentamethylenediamine, hexamethylenediamine, decamethylenediamine and dodecamethylenediamine.

The present invention therefore also provides a polymer film (P) in which component (B2) is selected from the group consisting of tetramethylenediamine, pentamethylenediamine, hexamethylenediamine, decamethylenediamine and dodecamethylenediamine.

Component (B3)

According to the invention, any component (B3) present in component (B) is at least one C₄-C₂₀ diacid.

In the context of the present invention, “at least one C₄-C₂₀ diacid” means either exactly one C₄-C₂₀ diacid or a mixture of two or more C₄-C₂₀ diacids.

In the context of the present invention, “C₄-C₂₀ diacid” is understood to mean aliphatic and/or aromatic compounds having 2 to 18 carbon atoms and two carboxyl groups (—COOH groups). The aliphatic and/or aromatic compounds may be unsubstituted or additionally at least monosubstituted. If the aliphatic and/or aromatic compounds are additionally at least monosubstituted, they may bear one, two or more substituents that do not take part in the polymerization of components (A) and (B). Substituents of this kind are, for example, alkyl or cycloalkyl substituents. These are known to those skilled in the art. Preferably, the at least one C₄-C₂₀ diacid is unsubstituted.

Suitable components (B3) are selected, for example, from the group consisting of butanedioic acid (succinic acid), pentanedioic acid (glutaric acid), hexanedioic acid (adipic acid), heptanedioic acid (pimelic acid), octanedioic acid (suberic acid), nonanedioic acid (azelaic acid), decanedioic acid (sebacic acid), undecanedioic acid, dodecanedioic acid, tridecanedioic acid, tetradecanedioic acid and hexadecanedioic acid.

Preferably, component (B3) is selected from the group consisting of pentanedioic acid (glutaric acid), hexanedioic acid (adipic acid), decanedioic acid (sebacic acid) and dodecanedioic acid.

Production of the Polymer Film (P)

The polymer film (P) is preferably produced in a process comprising the following steps:

-   i) providing at least one copolyamide; prepared by polymerization of     the following components:     -   (A) 15% to 84% by weight of at least one lactam,     -   (B) 16% to 85% by weight of a monomer mixture (M) comprising the         following components:         -   (B1) at least one C₃₂-C₄₀ dimer acid and         -   (B2) at least one C₄-C₁₂ diamine,     -   where the percentages by weight of components (A) and (B) are         based in each case on the sum total of the percentages by weight         of components (A) and (B), in molten form in a first extruder, -   ii) extruding the at least one copolyamide in molten form provided     in step i) out of the first extruder through a die to obtain a film     of the at least one copolyamide in molten form, -   iii) cooling the film obtained in step ii) of the at least one     copolyamide in molten form, with solidification of the at least one     copolyamide to obtain the polymer film (P).

The present invention therefore also provides a process for producing a polymer film (P) of the invention, comprising the steps of

-   i) providing at least one copolyamide prepared by polymerization of     the following components:     -   (A) 15% to 84% by weight of at least one lactam,     -   (B) 16% to 85% by weight of a monomer mixture (M) comprising the         following components:         -   (B1) at least one C₃₂-C₄₀ dimer acid and         -   (B2) at least one C₄-C₁₂ diamine,     -   where the percentages by weight of components (A) and (B) are         based in each case on the sum total of the percentages by weight         of components (A) and (B) in molten form in a first extruder, -   ii) extruding the at least one copolyamide in molten form provided     in step i) out of the first extruder through a die to obtain a film     of the at least one copolyamide in molten form, -   iii) cooling the film of the at least one copolyamide in molten form     obtained in step ii), with solidification of the at least one     copolyamide to obtain the polymer film (P).

In step i), the at least one copolyamide in molten form is provided in a first extruder.

In the context of the present invention, “a first extruder” means either exactly one first extruder or two or more first extruders. Typically, as many first extruders are used as first layers comprising the at least one copolyamide are to be present in the polymer film (P).

If the polymer film (P) is to comprise, for example, exactly one first layer comprising the at least one copolyamide, exactly one first extruder is used. If the polymer film (P) is to comprise exactly two first layers comprising the at least one copolyamide, exactly two first extruders are used. If the polymer film (P) is to comprise exactly five first layers comprising the at least one copolyamide, exactly five first extruders are used.

For example, 1 to 11 first extruders are used, preferably 1 to 5 first extruders and more preferably 1 to 3 first extruders.

In respect of the at least one copolyamide which is provided in step i), the above-described embodiments and preferences for the at least one copolyamide present in the polymer film (P) are correspondingly applicable.

According to the invention, the at least one copolyamide is provided in molten form.

In the context of the present invention, “in molten form” means that the at least one copolyamide is provided at a temperature above the melting temperature (T_(M(C))) of the at least one copolyamide. “In molten form” thus means that the at least one copolyamide is at a temperature above the melting temperature (T_(M(C))) of the at least one copolyamide. If the at least one copolyamide is in molten form, the at least one copolyamide is free-flowing.

“Free-flowing” means that the at least one copolyamide can be conveyed within the first extruder and that the at least one copolyamide can be extruded out of the first extruder.

For example, the at least one copolyamide is provided in step i) at a temperature in the range from 170 to 300° C., preferably in the range from 200 to 290° C. and especially preferably in the range from 230 to 280° C., in each case with the proviso that the temperature at which the at least one copolyamide is provided is above the melting temperature (T_(M(C))) of the at least one copolyamide.

The at least one copolyamide can be provided in molten form in the first extruder by any methods known to those skilled in the art.

For example, the at least one copolyamide can be supplied to the first extruder in molten form or in solid form. If the at least one copolyamide is supplied to the first extruder in solid form, it can be supplied to the first extruder, for example, in the form of pellets and/or in the form of powder. The at least one copolyamide is then melted in the first extruder and thus provided in molten form in the first extruder. This embodiment is preferred.

In addition, it is possible that components (A) and (B) are polymerized directly in the first extruder and the at least one copolyamide is thus provided in molten form in the first extruder. Processes for this purpose are known to those skilled in the art.

In step ii), the at least one copolyamide in molten form is extruded out of the first extruder through a die to obtain a film of the at least one copolyamide in molten form.

In the context of the present invention, “a die” means either exactly one die or two or more dies. Preference is given in accordance with the invention to exactly one die.

Suitable dies are all dies known to those skilled in the art that enable extrusion of a film composed of the at least one copolyamide in molten form. Examples of dies of this kind are annular dies or slot dies.

Suitable annular dies and slot dies are known as such to those skilled in the art.

If, for example, the step i1) described further down is conducted, it is preferable that, in step ii), the at least one copolyamide in molten form from the first extruder is combined with the at least one further polymer (FP) in molten form from the further extruder in the die, for example in the annular die or in the slot die.

More particularly, in step ii), the at least one copolyamide in molten form from the first extruder is combined with the at least one further polymer (FP) in molten form from the further extruder in the die in such a way that the film obtained in step ii) of the at least one copolyamide and the at least one further polymer (FP), each in molten form, comprises at least one first layer comprising the at least one copolyamide in molten form, and at least one further layer comprising the at least one further polymer (FP) in molten form.

For example, the thickness of the film of the at least one copolyamide in molten form is in the range from 0.1 μm to 1 mm, preferably in the range from 5 to 500 μm and especially preferably in the range from 20 to 100 μm.

The film of the at least one copolyamide in molten form may, for example, be a flat film or a tubular film. A tubular film is typically obtained when the die used is an annular die; a flat film is obtained when the die used is a slot die.

In step iii), the film obtained in step ii) of the at least one copolyamide in molten form is cooled down. This results in solidification of the at least one copolyamide to obtain the polymer film (P).

Suitable methods of cooling of the film of the at least one copolyamide in molten form are all those known to the person skilled in the art. For example, the film of the at least one copolyamide in molten form can be cooled by air or water cooling or by contact with a cold surface.

The film of the at least one copolyamide in molten form is cooled down in step iii), for example, to a temperature below the melting temperature (T_(M(C))) of the at least one copolyamide to obtain the polymer film (P). Preferably, the film of the at least one copolyamide in molten form in step iii) is cooled down to a temperature below the glass transition temperature (T_(G(C))) of the at least one copolyamide.

For example, the film of the at least one copolyamide in molten form is cooled down to a temperature in the range from 0 to 100° C., preferably in the range from 10 to 80° C. and especially preferably in the range from 15 to 50° C., the temperature to which the film of the at least one copolyamide in molten form is cooled down being below the melting temperature (T_(M(C))), preferably below the glass transition temperature (T_(G(C))), of the at least one copolyamide.

The present invention therefore also provides a process for producing a polymer film (P) in which, in step iii), the film of the at least one copolyamide in molten form is cooled down to a temperature below the melting temperature (T_(M(C))) of the at least one copolyamide.

In respect of the polymer film (P) obtained in step iii), the embodiments and preferences described in respect of the polymer film (P) of the invention are correspondingly applicable.

Steps ii) and iii) can be conducted successively or simultaneously.

Preference is given to additionally conducting a step i1) in which at least one further polymer (FP) in molten form is provided in a further extruder.

In that case, the process for producing the polymer film (P) comprises the following steps:

-   i) providing at least one copolyamide prepared by polymerizing the     following components:     -   (A) 15% to 84% by weight of at least one lactam,     -   (B) 16% to 85% by weight of a monomer mixture (M) comprising the         following components:         -   (B1) at least one C₃₂-C₄₀ dimer acid and         -   (B2) at least one C₄-C₁₂ diamine,     -   where the percentages by weight of components (A) and (B) are         each based on the sum total of the percentages by weight of         components (A) and (B), in molten form in a first extruder, -   i1) providing at least one further polymer (FP) in molten form in a     further extruder, -   ii) extruding the at least one copolyamide in molten form provided     in step i) out of the first extruder through a die and extruding the     at least one further polymer (FP) in molten form provided in step     i1) from the further extruder through the die to obtain a film of     the at least one copolyamide and the at least one further polymer     (FP), each in molten form, -   iii) cooling the film obtained in step ii) of the at least one     copolyamide and the at least one further polymer (FP), each in     molten form, with solidification of the at least one copolyamide     and/or the at least one further polymer (FP) to obtain the polymer     film (P).

In step i1), the at least one further polymer (FP) in molten form is provided in a further extruder.

In the context of the present invention, “a further extruder” means either exactly one further extruder or two or more further extruders. Preference is given to two or more further extruders.

Preference is given to using as many further extruders as further layers comprising the at least one further polymer (FP) are to be present in the polymer film (P). For example, 1 to 13 further extruders are used, preferably 1 to 11 further extruders and especially preferably 1 to 7 further extruders.

If the polymer film (P), for example, is to comprise exactly one further layer comprising the at least one further polymer (FP), exactly one further extruder is used. If the polymer film (P) is to comprise exactly two further layers comprising the at least one further polymer (FP), exactly two further extruders are used. If the polymer film (P) is to comprise exactly five further layers comprising the at least one further polymer (FP), exactly five further extruders are used.

In respect of the further extruder, the embodiments and preferences described above for the first extruder are correspondingly applicable.

In respect of the at least one further polymer (FP), the embodiments and preferences described above for the at least one further polymer (FP) that may be present in the polymer film (P) are correspondingly applicable.

According to the invention, the at least one further polymer (FP) in step i1) is provided in molten form. “In molten form” means the at least one further polymer (FP) is provided at a temperature above the melting temperature (T_(M(FP)))) of the at least one further polymer (FP). “In molten form” thus means that the at least one further polymer (FP) is at a temperature above the melting temperature (T_(M(FP))) of the at least one further polymer (FP). If the at least one further polymer (FP) is in molten form, the at least one further polymer (FP) is free-flowing.

“Free-flowing” means that the at least one further polymer (FP) can be conveyed within the further extruder and that the at least one further polymer (FP) can be extruded out of the further extruder.

For example, the at least one further polymer (FP) in step i1) is provided at a temperature in the range from 120 to 350° C., preferably in the range from 130 to 300° C. and especially preferably in the range from 140 to 250° C., in each case with the proviso that the temperature at which the at least one further polymer (FP) is provided is above the melting temperature (T_(M(FP))) of the at least one further polymer (FP).

The at least one further polymer (FP) may be provided in molten form in the further extruder by any methods known to those skilled in the art.

For example, the at least one further polymer (FP) can be supplied to the further extruder in molten form or in solid form. If the at least one further polymer (FP) is supplied to the further extruder in solid form, it can be supplied to the further extruder, for example, in the form of pellets and/or in the form of powder. In that case, the at least one further polymer (FP) is melted in the further extruder and thus provided in molten form in the further extruder.

Step i1) is typically conducted simultaneously with step i).

In respect of steps i), ii) and iii) the embodiments and preferences described above for steps i), ii) and iii) are applicable.

The film obtained in step ii) of the at least one copolyamide and of the at least one further polymer (FP), each in molten form, comprises the at least one copolyamide in at least one first layer and the at least one further polymer (FP) in at least one further layer. Typically, the film obtained in step ii) has as many first layers comprising the at least one copolyamide in molten form as first extruders were used in step i) and as many further layers comprising the at least one further polymer (FP) in molten form as further extruders were used in step i1).

It will be apparent that, when step i1) is conducted, the polymer film (P) obtained in step iii) is a multilayer film.

Preferably, the polymer film (P) is stretched. The polymer film (P) can be stretched after step iii); it is likewise possible to stretch the polymer film (P) during step iii), i.e. during the cooling of the film of the at least one copolyamide and optionally of the at least one further polymer (FP).

The present invention therefore also provides a process in which the following step is additionally conducted:

-   iv) stretching the polymer film (P) to obtain a stretched polymer     film (SP).

Steps iii) and iv) can be conducted successively or simultaneously.

In the stretching of the polymer film (P), the polymer chains of the at least one copolyamide become aligned and the crystallinity of the at least one copolyamide can increase.

It is additionally possible that the polymer chains of any at least one further polymer (FP) present in the polymer film (P) are aligned in the course of stretching. This can also increase the crystallinity of the at least one further polymer (FP).

The stretching can be effected by any methods known to those skilled in the art.

For example, the polymer film (P) can be stretched by guiding it over at least one roll, preferably a roll system, or by extending it widthwise. If the polymer film (P) is obtained in the form of a tube, it is likewise possible that the polymer film (P) is stretched by blowing air into the tube of the polymer film (P) and hence stretching the polymer film (P). It will be appreciated that combinations of the methods are also possible.

When the polymer film (P) is guided over at least one roll, preferably through a roll system, the polymer film (P) is stretched in extrusion direction, i.e. lengthwise. If the polymer film (P), by contrast, is extended widthwise, it is stretched at right angles to extrusion direction.

If the polymer film (P), for stretching, is guided over at least one roll, preferably through a roll system, the polymer chains of the at least one copolyamide and of any at least one further polymer (FP) are aligned parallel to the direction in which stretching is effected. The stretched polymer film (SP) obtained is then uniaxially oriented. The stretched polymer film obtained (SP) is likewise uniaxially oriented when the polymer film (P), for stretching, is extended widthwise. In that case too, the polymer chains of the at least one copolyamide and of any at least one further polymer (FP) are aligned parallel to the direction in which stretching is effected.

“Uniaxially oriented” means that the polymer chains are aligned essentially in one direction.

If the polymer film (P), for stretching, is guided over a roll system and additionally extended widthwise, the polymer chains of the at least one copolyamide and of any at least one further polymer (FP) are aligned parallel to both directions in which stretching is effected. The stretched polymer film (SP) obtained is then biaxially oriented.

“Biaxially oriented” means that the polymer chains are aligned essentially in two different directions, preferably at right angles to one another.

If the polymer film (P) is obtained in tubular form and the polymer film (P) is stretched by blowing air into the tube of the polymer film (P), the stretched polymer film (SP) obtained is uniaxially oriented.

If the above-described processes for stretching the polymer film (P) are combined, the polymer film (P) is thus obtained, for example, in tubular form and the polymer film (P) is stretched by blowing air into the tube of the polymer film (P) and simultaneously guided over rolls and likewise stretched; thus, the stretched polymer film (SP) obtained is biaxially oriented.

The polymer film (P) is typically stretched at a temperature above the glass transition temperature (T_(G(C))) of the at least one copolyamide and below the melting temperature (T_(M(C))) of the at least one copolyamide. It the polymer film (P) is a multilayer film, it is also preferable that the polymer film (P) is stretched at a temperature below the melting temperature (T_(M(FP))) of the at least one further polymer (FP), especially preferably at a temperature below the melting temperature of the at least one further polymer (FP) having the lowest melting temperature.

The polymer film (P) of the invention can be produced, for example, in a casting process, in a blowing process, in a biaxially oriented polyamide film process (BOPA process) or in a multifilm blowing process.

The present invention therefore also provides a polymer film (P) which is produced in a casting process, in a blowing process, in a biaxially oriented polyamide film process or in a multifilm blowing process.

The casting process, the blowing process the biaxially oriented polyamide film process and the multifilm blowing process are known as such to those skilled in the art. Typically, the polymer film (P) is stretched in these processes, such that a stretched polymer film (P) is obtained.

A casting process for producing the polymer film (P) preferably comprises the following steps i-c) to iv-c):

-   i-c) providing at least one copolyamide prepared by polymerizing the     following components:     -   (A) 15% to 84% by weight of at least one lactam,     -   (B) 16% to 85% by weight of a monomer mixture (M) comprising the         following components:         -   (B1) at least one C₃₂-C₄₀ dimer acid and         -   (B2) at least one C₄-C₁₂ diamine,     -   where the percentages by weight of components (A) and (B) are         each based on the sum total of the percentages by weight of         components (A) and (B), in molten form in a first extruder, -   ii-c) extruding the at least one copolyamide in molten form provided     in step i-c) out of the first extruder through a die to obtain a     film of the at least one copolyamide in molten form, -   iii-c) cooling the film of the at least one copolyamide in molten     form obtained in step ii-c), with solidification of the at least one     copolyamide to obtain the polymer film (P), -   iv-c) stretching the polymer film (P) obtained in step iii-c) by     guiding the polymer film (P) over at least one roll, preferably over     a roll system, to obtain a stretched polymer film (SP).

In respect of steps i-c) to iii-c) of the casting process, the embodiments and preferences described above for steps i) to iii) of the process for producing the polymer film (P) are correspondingly applicable.

The die used in the casting process in step ii-c) is typically a slot die. The film of the at least one copolyamide in molten form obtained in step ii-c) is therefore preferably a flat film, and so the polymer film (P) obtained in step iii-c) and the stretched polymer film (SP) obtained in step iv-c) are preferably flat films.

In the casting process, steps iii-c) and iv-c) can be conducted successively or simultaneously. Preferably, in the casting process, steps iii-c) and iv-c) are conducted simultaneously; especially preferably, steps iii-c) and iv-c) are conducted simultaneously and directly after step ii-c).

It is also preferable that, in the casting process, the at least one roll used in step iv-c), preferably the roll system, is cooled during step iv-c).

A blowing process for producing the polymer film (P) preferably comprises the following steps i-b) to iv-b):

-   i-b) providing at least one copolyamide prepared by polymerizing the     following components:     -   (A) 15% to 84% by weight of at least one lactam,     -   (B) 16% to 85% by weight of a monomer mixture (M) comprising the         following components:         -   (B1) at least one C₃₂-C₄₀ dimer acid and         -   (B2) at least one C₄-C₁₂ diamine,     -   where the percentages by weight of components (A) and (B) are         each based on the sum total of the percentages by weight of         components (A) and (B), in molten form in a first extruder, -   ii-b) extruding the at least one copolyamide in molten form provided     in step i-b) out of the first extruder through a die, which is an     annular die, to obtain a tubular film of the at least one     copolyamide in molten form, -   iii-b) cooling the tubular film of the at least one copolyamide in     molten form obtained in step ii-b), with solidification of the at     least one copolyamide to obtain the polymer film (P), -   iv-b) stretching the polymer film (P) obtained in step iii-b) by     blowing air into the tube of the polymer film (P) to obtain a     stretched polymer film (SP).

In respect of steps i-b) to iii-b) of the blowing process, the embodiments and preferences described above for steps i) to iii) of the process for producing the polymer film (P) are correspondingly applicable.

The die used in step ii-b) of the blowing process is preferably a stack die, a helical distributor die or a mixed form thereof. These dies are known to those skilled in the art and are described, for example, in “Blown Film Extrusion” by Kirk Cantor, 2nd Edition, Carl Hanser Verlag, Munich 2011.

Steps iii-b) and iv-b) in the blowing process can be conducted simultaneously or successively. Preferably, in the blowing process, steps iii-b) and iv-b) are conducted simultaneously.

It will be apparent that, when steps iii-b) and iv-b) in the blowing process are conducted simultaneously, the tubular film of the at least one copolyamide obtained in molten form in step ii-b) is cooled down in step iii-b) and simultaneously stretched by blowing air into the tubular film to obtain the stretched polymer film (SP).

A biaxially oriented polyamide film process for producing the polymer film (P) preferably comprises the following steps i-o) to iv-o):

-   i-o) providing at least one copolyamide prepared by polymerizing the     following components:     -   (A) 15% to 84% by weight of at least one lactam,     -   (B) 16% to 85% by weight of a monomer mixture (M) comprising the         following components:         -   (B1) at least one C₃₂-C₄₀ dimer acid and         -   (B2) at least one C₄-C₁₂ diamine,     -   where the percentages by weight of components (A) and (B) are         each based on the sum total of the percentages by weight of         components (A) and (B), in molten form in a first extruder, -   ii-o) extruding the at least one copolyamide in molten form provided     in step i-o) out of the first extruder through a die to obtain a     film of the at least one copolyamide in molten form, -   iii-o) cooling the film of the at least one copolyamide in molten     form obtained in step ii-o), with solidification of the at least one     copolyamide to obtain the polymer film (P), -   iv-o) stretching the polymer film (P) obtained in step iii-o) by     guiding the polymer film (P) over at least one roll, preferably over     a roll system, and lengthening the width thereof to obtain the     stretched polymer film (SP).

In respect of steps i-o) to iii-o) of the biaxially oriented polyamide film process, the embodiments and preferences described above for steps i) to iii) of the process for producing the polymer film (P) are correspondingly applicable.

The die used in the biaxially oriented polyamide film process in step ii-o) is typically a slot die. The film of the at least one copolyamide in molten form obtained in step ii-o) is therefore preferably a flat film, and so the polymer film (P) obtained in step iii-o) and the stretched polymer film (SP) obtained in step iv-o) are preferably flat films.

In the biaxially oriented polyamide film process, steps iii-o) and iv-o) can be conducted successively or simultaneously; preference is given to conducting steps iii-o) and iv-o) successively. Especially preferably, in the biaxially oriented polyamide film process, steps iii-o) and iv-o) are conducted successively and the polymer film (P) obtained in step iii-o) is heated prior to step iv-o). It is preferable here that the polymer film (P) is heated prior to step iv-o) to a temperature above the glass transition temperature (T_(G(C))) of the at least one copolyamide present in the polymer film (P) and below the melting temperature (T_(M(C))) of the at least one copolyamide present in the polymer film (P). The polymer film (P) is then preferably stretched in step iv-o) at the temperature to which it is heated prior to step iv-o).

A multifilm blowing process for producing the polymer film (P) preferably comprises the following steps i-m) to iv-m):

-   i-m) providing at least one copolyamide prepared by polymerizing the     following components:     -   (A) 15% to 84% by weight of at least one lactam,     -   (B) 16% to 85% by weight of a monomer mixture (M) comprising the         following components:         -   (B1) at least one C₃₂-C₄₀ dimer acid and         -   (B2) at least one C₄-C₁₂ diamine,     -   where the percentages by weight of components (A) and (B) are         each based on the sum total of the percentages by weight of         components (A) and (B), in molten form in a first extruder, -   ii-m) extruding the at least one copolyamide in molten form provided     in step i-m) out of the first extruder through a die, which is an     annular die, to obtain a tubular film of the at least one     copolyamide in molten form, -   iii-m) cooling the tubular film of the at least one copolyamide in     molten form obtained in step ii-m), with solidification of the at     least one copolyamide to obtain the polymer film (P), -   iv-m) stretching the polymer film (P) obtained in step iii-m) by     blowing air into the tube of the polymer film (P) and by at the same     time guiding the polymer film (P) over at least one roll, preferably     over a roll system, to obtain a stretched polymer film (SP).

In respect of steps i-m) to iii-m) of the multifilm blowing process, the embodiments and preferences described above for steps i) to iii) of the process for producing the polymer film (P) are correspondingly applicable.

Preferably, the tubular film of the at least one copolyamide in molten form is cooled down in a water bath in step iii-m).

In the multifilm blowing process, steps iii-m) and iv-m) can be conducted successively or simultaneously; preference is given to conducting steps iii-m) and iv-m) successively. Especially preferably, steps iii-m) and iv-m) are conducted successively and the polymer film (P) obtained in step iii-m) is heated prior to step iv-m). It is preferable here that the polymer film (P) is heated prior to step iv-m) to a temperature above the glass transition temperature (T_(G(C))) of the at least one copolyamide present in the polymer film (P) and below the melting temperature (T_(M(C))) of the at least one copolyamide present in the polymer film (P). The polymer film (P) is then preferably stretched in step iv-m) at the temperature to which it is heated prior to step iv-m).

It will be apparent that, in the casting process, in the blowing process, in the biaxially oriented polyamide film process and in the multifilm blowing process it is likewise optionally possible to conduct step) in which at least one further polymer (FP) is provided in molten form in a further extruder and that in that case, correspondingly, step ii) of the process for producing the polymer film (P), in step ii-c), in step ii-b) in step ii-o) and in step ii-m), a film of the at least one copolyamide and of the at least one further polymer (FP), each in molten form, is obtained and this is cooled down in accordance with step iii) of the process for producing the polymer film (P) in step iii-c), in step iii-b) in step ii-o) and in step ii-m).

In respect of the optionally conducted step i1), the embodiments and preferences described above for the optionally conducted step i1) of the process for producing the polymer film (P) are correspondingly applicable.

Preferably, no step i1) is conducted in the biaxially oriented polyamide film process. Preferably, there is thus no further polymer (FP) provided in a further extruder in the biaxially oriented polyamide film process.

The stretched polymer film (P) obtained can, for example, be wound up subsequently to its production. Methods for this purpose are known to those skilled in the art. If the stretched polymer film (SP) is obtained in tubular form, as, for example, in the blowing process and in the multifilm blowing process, the tube can also be slit before being wound up. A slit film can then be wound up on one or more rolls.

Use of the Polymer Film

The polymer film (P) of the invention is preferably used as packaging film.

The present invention therefore also provides for the use of the polymer film (P) of the invention as packaging film.

For example, the polymer film (P) of the invention can be used as tubular pouch packaging, as laterally sealed pouch packaging, as thermoformed packaging, for closable pouches and/or as cushion packaging.

The present invention is elucidated in detail hereinafter with reference to examples.

EXAMPLES

The properties of the polymer films (P) were determined as follows:

The viscosity number of copolyamides comprising units derived from a C₃₂-C₄₀ dimer acid was determined in a 0.5% by weight solution of phenol/o-dichlorobenzene in a weight ratio of 1:1 at 25° C.

The viscosity number of copolyamides and polyimides that do not comprise any units derived from a C₃₂-C₄₀ dimer acid was determined in a 0.5% by weight solution in 96% by weight sulfuric acid at 25° C. according to EN ISO 307: 2007+Amd 1: 2013.

The glass transition temperatures and melting temperatures were determined according to ISO 11357-1: 2009, ISO 11357-2: 2013 and ISO 11357-3: 2011. For this purpose, two heating runs were conducted and the glass transition and melting temperatures were ascertained from the second heating run.

The densities of the polyamides were determined by the gas pycnometer method according to EN ISO 1183-3: 1999.

For determination of the proportion of polyamide-6,36 in the copolyamide, the copolyamide was hydrolyzed in dilute hydrochloric acid (20%). This protonates the units derived from hexamethylenediamine, with the chloride ion from the hydrochloric acid forming the counterion. By means of ion exchanger, this chloride ion was then exchanged for a hydroxide ion with release of hexamethylenediamine. By titration with 0.1 molar hydrochloric acid, the hexamethylenediamine concentration is then determined, from which the proportion of polyamide-6,36 in the copolyamide can be determined.

Tear propagation resistance is determined according to Elmendorf, DIN ISO 6383-2: 2004 in extrusion direction (MD) and at right angles thereto (TD). The films were conditioned under standard climatic conditions for non-tropical countries according to DIN EN ISO 291: 2008.

Modulus of elasticity is determined according to ISO 527-3: 1995.

The impact resistance of the polymer film (P) was determined according to DIN ISO 7765-2: 1994 with 5 specimens at a relative air humidity of 0%, with reporting of the puncture energy in the present context.

The following polymers were used:

Polyamides

-   P-1 nylon-6 from BASF SE®, sold under the Ultramid B40L brand name,     with a viscosity number of 250 mL/g, a glass transition temperature     of 57° C., a melting temperature of 220° C. and a density of 1.153     g/mL. -   P-2 nylon-6 from BASF SE®, sold under the Ultramid B33L brand name,     with a viscosity number of 195 mL/g, a glass transition temperature     of 56° C., a melting temperature of 220° C. and a density of 1.145     g/mL. -   P-3 copolymer of nylon-6 and nylon-6,6 (PA 6/6.6) from BASF SE®,     sold under the Ultramid C40L brand name, with a viscosity number of     250 mL/g, a glass transition temperature of 53° C., a melting     temperature of 190° C. and a density of 1.143 g/mL. -   P-4 copolymer of nylon-6 and nylon-6,6 (PA 6/6.6) from BASF SE®,     sold under the Ultramid C33L brand name, with a viscosity number of     195 mL/g, a glass transition temperature of 55° C., a melting     temperature of 196° C. and a density of 1.144 g/mL.     Copolyamides with Dimer Acid: -   C-1 A copolyamide of nylon-6 and polyamide-6,36, prepared by the     following method:     -   900 kg of caprolactam (component (A)), 83.5 kg of Pripol 1009         from Croda (C₃₆ dimer acid, hydrogenated, component (B1)), 19.9         kg of 85% by weight hexamethylenediamine solution (component         (B2)) in water, 100 g of Polyapp 2557-CTW antifoam reagent         composed of polymethylsiloxane from Polystell do Brazil and 100         kg of water were mixed in a 1930 L tank and blanketed with         nitrogen. The outside temperature of the tank was heated to         290° C. and the mixture present in the tank was stirred at this         temperature for 11 hours. In the first 7 h the mixture was         stirred at elevated pressure, in the next 4 hours under reduced         pressure, during which the water formed was distilled off. The         copolyamide thus obtained was then discharged from the tank,         extruded and pelletized. After the pellets of the copolyamide         obtained had been extracted with water at 95° C. for 4×6 hours,         the copolyamide was dried at 90 to 140° C. in a nitrogen stream         for 10 hours. The viscosity number was 246 mL/g, the glass         transition temperature was 49° C. and the melting temperature         was 211° C. The proportion of polyamide-6,36 in the copolyamide,         based on the total weight of the copolyamide, was 10.5% by         weight; the density was 1.116 g/mL. -   C-2 A copolyamide of nylon-6 and polyamide-6,36, prepared by the     following method:     -   1039 kg of caprolactam (component (A)), 216 kg of Pripol 1009         from Croda (C₃₆ dimer acid, hydrogenated, component (B1)), 51.7         kg of 85% by weight hexamethylenediamine solution (component         (B2)) in water, 100 g of Polyapp 2557-CTW antifoam reagent from         Polystell do Brazil and 142 kg of water were mixed in a 1930 L         tank and blanketed with nitrogen. The outside temperature of the         tank was heated to 290° C. and the mixture was stirred at this         temperature for 11 hours. In the first 7 h the mixture was         stirred at elevated pressure, in the next 4 hours under reduced         pressure, during which the water formed was distilled off. The         copolyamide obtained was discharged from the tank, extruded and         pelletized. The pellets of the copolyamide obtained were         extracted with water at 95° C. for 4×6 hours and then dried at         90 to 140° C. in a nitrogen stream for 10 hours. The copolyamide         obtained had a viscosity number of 244 mL/g, a glass transition         temperature of 44° C. and a melting temperature of 203° C. The         proportion of polyamide-6,36 in the copolyamide, based on the         total weight of the copolyamide, was 20.8% by weight; the         density was 1.095 g/mL. -   C-3 A copolyamide of nylon-6 and polyamide-6,36, prepared by the     following method:     -   932 kg of caprolactam (component (A)), 323.2 kg of Pripol 1009         from Croda (C₃₆ dimer acid, hydrogenated, component (B1)), 77.84         kg of 85% by weight hexamethylenediamine solution (component         (B2)) in water and 153 kg of water were mixed in a 1930 L tank         and blanketed with nitrogen. The outside temperature of the tank         was heated to 290° C. and the mixture was stirred at this         temperature for 11 hours. In the first 7 h the mixture was         stirred at elevated pressure, in the next 4 hours under reduced         pressure, during which water formed was distilled off. The         copolyamide obtained was discharged from the tank, extruded and         pelletized. The pellets of the copolyamide obtained were         extracted with water at 95° C. for 4×6 hours and then dried at         90 to 140° C. in a nitrogen stream for 10 hours. The copolyamide         obtained had a viscosity number of 259 mL/g, a glass transition         temperature of 38° C. and a melting temperature of 188° C. The         proportion of polyamide-6,36 in the copolyamide, based on the         total weight of the copolyamide, was 30.3% by weight; the         density was 1.076 g/mL. -   C-4 A copolyamide of nylon-6 and polyamide-6,36, prepared by the     following method:     -   932 kg of caprolactam (component (A)), 322 kg of Empol 1061 from         BASF SE (C₃₆ dimer acid, unhydrogenated, component (B1)), 77.84         kg of 85% by weight hexamethylenediamine solution (component         (B2)) in water and 153 kg of water were mixed in a 1930 L tank         and blanketed with nitrogen. The outside temperature of the tank         was heated to 290° C. and the mixture was stirred at this         temperature for 11 hours. In the first 7 h the mixture was         stirred at elevated pressure, in the next 4 hours under reduced         pressure, during which water formed was distilled off. The         copolyamide obtained was discharged from the tank, extruded and         pelletized. The pellets of the copolyamide obtained were         extracted with water at 95° C. for 4×6 hours and then dried at         90 to 140° C. in a nitrogen stream for 10 hours. The copolyamide         obtained had a viscosity number of 212 mL/g, a glass transition         temperature of 38° C. and a melting temperature of 187° C. The         proportion of polyamide-6,36 in the copolyamide, based on the         total weight of the copolyamide, was 28.9% by weight; the         density was 1.076 g/mL.         Further Polymer (FP) -   FP-1 Low-density polyethylene (LDPE) from LyondellBasell®, sold     under the Lupolen 2420 F brand name with an MFR (melt flow rate)     (190° C./2.16 kg) of 0.75 g/10 min. -   FP-2 Low-density polyethylene (LDPE) from LyondellBasell®, sold     under the Lupolen 3020 K brand name with an MFR (melt flow rate)     (190° C./2.16 kg) of 4 g/10 min. -   FP-3 Anhydride-modified linear low-density polyethylene (LLDPE) from     DuPont®, sold under the Bynel 4104 brand name with an MFR (melt flow     rate) (190° C./2.16 kg) of 1.1 g/10 min. -   FP-4 Anhydride-modified linear low-density polyethylene (LLDPE) from     DuPont®, sold under the Bynel 4105 brand name with an MFR (melt flow     rate) (190° C./2.16 kg) of 4 g/10 min. -   FP-5 A poly(ethyl-vinyl alcohol) (EVOH) from Kuraray®, sold under     the EVAL F171B brand name with an MFR (melt flow rate) (210° C./2.16     kg) of 1.8 g/10 min and an ethylene content of 32 mol %. -   FP-6 A poly(ethyl-vinyl alcohol) (EVOH) from Kuraray®, sold under     the EVAL L171B brand name with an MFR (melt flow rate) (210° C./2.16     kg) of 4 g/10 min and an ethylene content of 27 mol %.     Production of Monofilms by a Casting Process

For production of monofilms, a 7-layer cast film system from Collin® with a die head width of 800 mm was used. Thus, 7 extruders were used. 6 of the extruders had a diameter of 30 mm (extruders B, C, D, E, F, G); one extruder had a diameter of 45 mm (extruder A). Each of the 7 extruders were loaded with the same component. The melt from extruder A was in contact with the casting roll; the melt from extruder G was the furthest removed therefrom. The sequence of the layers was A, B, C, D, E, F, G. The polymer films produced had a thickness of 100 μm and the layers had a layer thickness of 15/14/14/14/14/14/15 μm. The components used and the results of the measurement of the tear propagation resistance, modulus of elasticity and puncture resistance are specified in table 1. The percentages by weight of component (B) specified in table 1 are understood to mean the percentages by weight of units derived from component (B) (polyamide-6,36 units) in the copolyamide, based on the total weight of the copolyamide.

TABLE 1 V1 V2 V3 B4 B5 Component P-2 P-4 C-1 C-2 C-3 Component (B) [% by wt.] — — 10.5 20.8 30.3 Tear [mN] 2337 2601 3076 6329 7706 propagation (8 N (8 N (8 N (32 N (32 N resistance pendulum) pendulum) pendulum) pendulum) pendulum) (MD) Tear [mN] 2046 3337 2734 6087 7588 propagation (8 N (8 N (8 N (8 N (8 N resistance (TD) pendulum) pendulum) pendulum) pendulum) pendulum) Modulus of [MPa] 758 439 713 621 514 elasticity (MD) Modulus of [MPa] 756 469 684 621 365 elasticity (TD) Production of Multilayer Films by a Casting Process

Multilayer films comprising three different polymers were produced in the above-described 7-layer cast film system from Collin®. The multilayer films obtained had a thickness of 100 μm and the layers had a layer thickness of 15/14/14/14/14/14/15 μm. The extruders of the cast film system were charged with the components in accordance with the makeup of the multilayer films specified in table 2. The percentages by weight of component (B) specified in table 2 are understood to mean the percentages by weight of units derived from component (B) (polyamide-6,36 units) in the copolyamide, based on the total weight of the copolyamide. Table 2 also states the properties of the multilayer film produced.

TABLE 2 V6 V7 V8 B9 B10 Makeup FP-2 // FP-4 // FP-2 // FP-4 // FP-2 // FP-4 // FP-2 // FP-4 // FP-2 // FP-4 // P-2 // P-2 // P-2 // P-4 // P-4 // P-4 // C-1 // C-1 // C-1 // C-2 // C-2 // C-2 // C-3 // C-3 // C-3 // FP-4 // FP-2 FP-4 // FP-2 FP-4 // FP-2 FP-4 // FP-2 FP-4 // FP-2 Component (B) [% by wt.] — — 10.5 20.8 30.3 Tear [mN] 1293 1850 1702 2841 5874 propagation (8 N pendulum) (8 N pendulum) (8 N pendulum) (8 N pendulum) (8 N pendulum) resistance (MD) Tear [mN] 1438 1998 2131 3709 15856 propagation (8 N pendulum) (8 N pendulum) (8 N pendulum) (8 N pendulum) (32 N pendulum) resistance (TD) Puncture energy [J] 0.3 0.3 0.3 1.4 2.1 Modulus of [MPa] 437 347 431 408 353 elasticity (MD) Modulus of [MPa] 432 344 442 403 328 elasticity (TD) Production of Multilayer Films by a Casting Process

Multilayer films comprising five different polymers were produced in the above-described 7-layer cast film system from Collin®. The multilayer films obtained had a thickness of 100 μm and the layers had a layer thickness of 15/14/14/14/14/14/15 μm. The extruders of the cast film system were charged with the components in accordance with the makeup of the multilayer films specified in table 3. The percentages by weight of component (B) specified in table 3 are understood to mean the percentages by weight of units derived from component (B) (polyamide-6,36 units) in the copolyamide, based on the total weight of the copolyamide. Table 3 also states the properties of the multilayer film produced.

TABLE 3 V11 V12 V13 B14 B15 Makeup FP-2 // FP-4 // FP-2 // FP-4 // FP-2 // FP-4 // FP-2 // FP-4 // FP-2 // FP-4 // P-2 // FP-6 // P-2 P-4 // FP-6 // P-4 // C-1 // FP-6 // C-1 // C-2 // FP-6 // C-2 // C-3 // FP-6 // C-3 // // FP-4 // FP-2 FP-4 // FP-2 FP-4 // FP-2 FP-4 // FP-2 FP-4 // FP-2 Component (B) [% by wt.] — — 10.5 20.8 30.3 Tear propagation [mN] 3649 4344 4257 13206 11311 resistance (MD) (8 N pendulum) (8 N pendulum) (8 N pendulum) (32 N pendulum) (32 N pendulum) Tear propagation [mN] 3909 8812 6667 17953 14408 resistance (TD) (8 N pendulum) (32 N pendulum) (32 N pendulum) (8 N pendulum) (32 N pendulum) Modulus of [MPa] 717 629 723 698 628 elasticity (MD) Modulus of [MPa] 721 650 721 679 681 elasticity (TD) Production of Monofilms by the Blowing Process

Monofilms were produced in a 7-layer blown film system from Collin® having a die head diameter of 180 mm. Of the 7 extruders, 6 had a diameter of 30 mm (extruders B, C, D, E, F, G) and one a diameter of 45 mm (extruder A). The melt from extruder was on the inside of the bubble; the melt from extruder G was on the outside. The sequence of the layers, from the inside outward, was A, B, C, D, E, F, G. The monofilms produced had a thickness of 100 μm and the layers had a layer thickness of 15/14/14/14/14/14/15 μm in the monofilms. All the extruders were loaded with the same component. The films were slit before they were wound up.

The components used and the properties of the monomaterial films are specified in table 4. The percentages by weight of component (B) specified in table 4 are understood to mean the percentages by weight of units derived from component (B) (polyamide-6,36 units) in the copolyamide, based on the total weight of the copolyamide.

TABLE 4 V16 V17 V18 B19 B20 Component P-1 P-3 C-1 C-2 C-3 Component (B) [% by — — 10.5 20.8 30.3 wt.] Tear [mN] 1913 4783 3083 3804 9548 propagation (8 N (8 N (8 N (32 N (32 N resistance (MD) pendulum) pendulum) pendulum) pendulum) pendulum) Tear [mN] 1823 5325 2909 5767 22287 propagation (8 N (8 N (8 N (8 N (8 N resistance (TD) pendulum) pendulum) pendulum) pendulum) pendulum) Modulus of [MPa] 635 411 536 412 329 elasticity (MD) Modulus of [MPa] 656 410 510 446 356 elasticity (TD) Production of Multilayer Films in a Blowing Process

Multilayer films comprising three different materials were produced in a 7-layer blown film system from Collin® with a die head diameter of 180 mm. Of the 7 extruders, 6 had a diameter of 30 mm and one a diameter of 45 mm. The multilayer films obtained had a thickness of 100 μm and the layers had a layer thickness of 15/14/14/14/14/15 μm. The extruders of the blown film system were charged with the components in accordance with the makeup of the multilayer films specified in table 5. Table 5 also states the properties of the multilayer films produced. The percentages by weight of component (B) specified in table 5 are understood to mean the percentages by weight of units derived from component (B) (polyamide-6,36 units) in the copolyamide, based on the total weight of the copolyamide.

TABLE 5 V21 V22 V23 B24 B25 Makeup FP-1 // FP-3 // FP-1 // FP-3 // FP-1 // FP-3 // FP-1 // FP-3 // FP-1 // FP-3 // P-1 // P-1 // P-1 // P-3 // P-3 // P-3 // C-1 // C-1 // C-1 // C-2 // C-2 // C-2 // C-3 // C-3 // C-3 // FP-3 // FP-1 FP-3 // FP-1 FP-3 // FP-1 FP-3 // FP-1 FP-3 // FP-1 Component (B) [% by — — 10.5 20.8 30.3 wt.] Tear propagation [mN] 1461 2826 1950 3109 5181 resistance (MD) (8 N pendulum) (8 N pendulum) (8 N pendulum) (8 N pendulum) (8 N pendulum) Tear propagation [mN] 1461 2824 2122 3468 4318 resistance (TD) (8 N pendulum) (8 N pendulum) (8 N pendulum) (8 N pendulum) (8 N pendulum) Puncture energy [J] 1.3 0.6 1.3 3.7 4.0 Modulus of [MPa] 377 312 321 316 280 elasticity (MD) Modulus of [MPa] 391 307 356 326 307 elasticity (TD) Production of Multilayer Films in a Blowing Process

Multilayer films comprising five different polymers were produced in a 7-layer blown film system from Collin® with a die head diameter of 180 mm. Of the 7 extruders, 6 had a diameter of 30 mm and one a diameter of 45 mm. The multilayer films obtained had a thickness of 100 μm and the layers had a layer thickness of 15/14/14/14/14/15 μm. The extruders of the blown film system were charged with the components in accordance with the makeup of the multilayer films specified in table 6. Table 6 also states the properties of the multilayer films produced. The percentages by weight of component (B) specified in table 6 are understood to mean the percentages by weight of units derived from component (B) (polyamide-6,36 units) in the copolyamide, based on the total weight of the copolyamide.

TABLE 6 V26 V27 V28 B29 B30 Makeup FP-1 // FP-3 // FP-1 // FP-3 // FP-1 // FP-3 // FP-1 // FP-3 // FP-1 // FP-3 // P-1 // FP-5 // P-1 // P-3 // FP-5 // P-3 // C-1 // FP-5 // C-1 // C-2 // FP-5 // C-2 // C-3 // FP-5 // C-3 // FP-3 // FP-1 FP-3 // FP-1 FP-3 // FP-1 FP-3 // FP-1 FP-3 // FP-1 Component (B) [% by — — 10.5 20.8 30.3 wt.] Tear propagation [mN] 1975 6401 1875 6194 10042 resistance (MD) (8 N pendulum) (32 N pendulum) (8 N pendulum) (32 N pendulum) (32 N pendulum) Tear propagation [mN] 2325 8062 1975 9637 13530 resistance (TD) (8 N pendulum) (8 N pendulum) (8 N pendulum) (8 N pendulum) (8 N pendulum) Puncture energy [J] 0.7 0.8 1.2 1.2 0.9 Modulus of [MPa] 814 709 878 778 714 elasticity (MD) Modulus of [MPa] 793 710 421 672 593 elasticity (TD) Production of Monofilms in the Blowing Process

Monofilms were produced in a 7-layer blown film system from Collin® with a die head diameter of 180 mm. Of the 7 extruders, 6 had a diameter of 30 mm and one a diameter of 45 mm. The monomaterial films produced had a thickness of 100 μm and the layers had a layer thickness of 15/14/14/14/14/14/15 μm. All the extruders were loaded with the same component.

The components used and the properties of the monofilms are specified in table 7. The percentages by weight of component (B) specified in table 7 are understood to mean the percentages by weight of units derived from component (B) (polyamide-6,36 units) in the copolyamide, based on the total weight of the copolyamide.

TABLE 7 V31 V32 B33 Component P-1 P-3 C-4 Component (B) [% by — — 28.9 wt.] Tear propagation [mN] 1910 4408 8654 resistance (MD) (8N pendulum) (8N (32N pendulum) pendulum) Tear propagation [mN] 1736 4057 11436 resistance (TD) (8N pendulum) (8N (32N pendulum) pendulum) Modulus of elasticity [MPa] 666 484 297 (MD) Modulus of elasticity [MPa] 678 457 299 (TD) Production of Multilayer Films in the Blowing Process

Multilayer films were produced in a 7-layer blown film system from Collin® with a die head diameter of 180 mm. Of the 7 extruders, 6 had a diameter of 30 mm and one a diameter of 45 mm. The monomaterial films produced had a thickness of 100 μm and the layers had a layer thickness of 15/14/14/14/14/14/15 μm. All the extruders were loaded with the same component.

The components used and the properties of the monomaterial films are specified in table 8. The percentages by weight of component (B) specified in table 8 are understood to mean the percentages by weight of units derived from component (B) (polyamide-6,36 units) in the copolyamide, based on the total weight of the copolyamide.

TABLE 8 V34 V35 B36 Makeup FP-1 // FP-3 // FP-1 // FP-3 // FP-1 // FP-3 // P-1 // FP-5 // P-1 // P-3 // FP-5 // P-3 // C-4 // FP-5 // C-4 // FP-3 // FP-1 FP-3 // FP-1 FP-3 // FP-1 Component (B) [% by — — 28.9 wt.] Tear propagation [mN] 1932 3079 15149 resistance (MD) (8N pendulum) (32N pendulum) (32N pendulum) Tear propagation [mN] 2276 6124 10110 resistance (TD) (8N pendulum) (8N pendulum) (32N pendulum) Modulus of [MPa] 990 824 746 elasticity (MD) Modulus of [MPa] 966 784 728 elasticity (TD)

The above examples show that the copolyamide of the invention can significantly increase the tear propagation resistance of the polymer films (P) both in extrusion direction and at right angles thereto. The modulus of elasticity and puncture resistance of the polymer films (P) of the invention are also within a range acceptable for practical use, and so the polymer films (P) of the invention have advantageous properties overall, especially as packaging films. 

The invention claimed is:
 1. A polymer film, comprising: a copolyamide, which is prepared by polymerizing components: (A) from 15% to 84% by weight of at least one lactam, (B) from 16% to 85% by weight of a monomer mixture consisting of components: (B1) a C₃₂-C₄₀ dimer acid; and (B2) a C₄-C₁₂ diamine, and (B3) optionally a C₄-C₂₀ diacid; wherein percentages by weight of the components (A) and (B) are based on a total weight of the components (A) and (B), and if (B3) is not present in component (B), component (B) consists of 45 to 55 mol % of component (B1) and 45 to 55 mol % of component (B2), based in each case on the total molar amount of component (B), or if (B3) is present in component (B), component (B) consists of 13 to 52.9 mol % of component (B1), 47 to 53 mol % of component (B2), and 0.1 to 13 mol % of component (B3), based in each case on the total molar amount of component (B); wherein the copolyamide has a viscosity number in the range from 160 to 290 mL/g, determined in a 0.5% by weight solution of the copolyamide in a mixture of phenol/o-dichlorobenzene in a weight ratio of 1:1.
 2. The polymer film according to claim 1, wherein the component (A) is selected from the group consisting of 3-aminopropanolactam, 4-aminobutanolactam, 5-aminopentanolactam, 6-aminohexanolactam, 7-aminoheptanolactam, 8-aminooctanolactam, 9-aminononanolactam, 10-aminodecanolactam, 11-aminoundecanolactam and 12-aminododecanolactam.
 3. The polymer film according to claim 1, wherein the component (B) consists of from 45 to 55 mol % of the component (B1) and from 45 to 55 mol % of the component (B2), based on a total molar amount of the component (B).
 4. The polymer film according to claim 1, wherein the component (B2) is selected from the group consisting of tetramethylenediamine, pentamethylenediamine, hexamethylenediamine, decamethylenediamine and dodecamethylenediamine.
 5. The polymer film according to claim 1, wherein the component (B1) is prepared from one or more unsaturated fatty acids selected from the group consisting of an unsaturated C₁₆ fatty acid, an unsaturated C₁₈ fatty acid, and an unsaturated C₂₀ fatty acid.
 6. The polymer film according to claim 1, wherein the copolyamide has a glass transition temperature ranging from 20 to 50° C.
 7. The polymer film according to claim 1, wherein the copolyamide has a melting temperature ranging from 150 to 210° C.
 8. The polymer film according to claim 1, comprising: a first layer comprising the copolyamide, and an additional layer, wherein the additional layer comprises an additional polymer selected from the group consisting of a polyolefin, a poly(ethylene-vinyl alcohol), a poly(ethylene-vinyl acetate), a polyethylene terephthalate, a polyvinylidene chloride and a maleic anhydride-grafted polyolefin.
 9. The polymer film according to claim 1, produced in a casting process, in a blowing process, in a biaxially oriented polyamide film process, or in multifilm blowing process.
 10. The polymer film according to claim 1, wherein the polymer film has a thickness ranging from 0.1 μm to 1 mm.
 11. The polymer film according to claim 1, wherein the copolyamide is a random copolymer.
 12. A process for producing the polymer film according to claim 1, comprising: preparing the copolyamide in a molten form in a first extruder, extruding the copolyamide in the molten form out of the first extruder through a die to obtain a film of the copolyamide in the molten form, and cooling the film of the copolyamide in the molten form, with solidification of the copolyamide to obtain the polymer film.
 13. A packaging film, comprising the polymer film according to claim
 1. 